Kanish Metals, a reliable manufacturer and supplier in Dubai, UAE, provides Stainless Steel Forged Bars and Rods for high-performance use in numerous industries. Our forged rods and bars are constructed with high-quality stainless steel, offering top-notch strength, resistance to corrosion, and durability. They are produced with the help of innovative forging processes for uniformity, accuracy, and mechanical strength. It comes in several grades and sizes and provides high-quality stainless steel forged bars and rods apt for extreme applications in the aerospace, automotive, chemical, and manufacturing sectors.
Stainless Steel Forged Bars and Rods are manufactured from a range of stainless steel alloys, including 304, 316, 410, and 17-4PH. The alloys comprise chromium (10.5-30%), nickel (35%), and different amounts of carbon, manganese, and molybdenum. The bars and rods provide tensile strength ranging from 500-1150 MPa and yield strength ranging from 200-800 MPa, based on the grade. Their high resistance to corrosion, toughness, and hardness level up to 38 HRC render them appropriate for applications under high stress. They also show high resistance to wear and fatigue.
Standards : ASTM A276, ASTM A484, AISI
Grade : 201, 202, 301, 302, 303, 304, 304H, 304L, 316, 316H, 316L, 309, 309S, 310, 310S, 316Ti, 317, 317L, 347, 321, 321H, 410, 416, 420, 430, 430F, 431, 440C, 630, 17-4PH, F51
Range : from 2.00mm to 6.35mm (0.078″ to 0.25″)dia.
Tolerance : DIN 671, ASTM A484 & as per customer’s specific requirement.
Finish : Cold drawn, Centreless Ground, Polished
| Grade | Su | C | Si | P | Cr | Ni | M | Mo | Other |
|---|---|---|---|---|---|---|---|---|---|
| 316 | 0.030 max | 0.08 max | 0.75 max | 0.045 max | 16.0-18.0 | 10.0 14.0 | 2.00 max | 2.0 3.0 | – |
| 317L | 0.030 max | 0.035 max | 0.75 max | 0.045 max | 18.0-20.0 | 11.0 14.0 | 2.00 max | 3.0 4.0 | – |
| 304 | 0.030 max | 0.08 max | 0.75 max | 0.045 max | 18.0-20.0 | 8.0 11.0 | 2.00 max | – | – |
| 310 S | 0.030 max | 0.08 max | 1.5 max | 0.045 max | 24.0-26.0 | 19.0 22.0 | 2.00 max | 3.0 4.0 | – |
| 347 H | 0.030 max | 0.04 0.10 | 0.75 max | 0.045 max | 17.0- 19.0 | 9.0 13.0 | 2.00 max | – | 10C(Cb+Ta)<1.10% |
| 321 | 0.030 max | 0.08 | 0.75 max | 0.045 max | 17.0-20.0 | 9.0 12.0 | 2.00 max | – | 5C 0.70% |
| Grade | Tensile Strength | Yield Strength (0.2%Offset) | Density | Elongation | Melting Point |
|---|---|---|---|---|---|
| SS 303 | Psi – 85,000 | Psi – 45,000 | 55% | 50 % | Rb 180 |
| SS 202 | 515 MPa | 275 MPa | 8.0 g/cm3 | 40 % | 1454 °C |
| SS 304 | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 8.0 g/cm3 | 40% | 1400 °C |
| SS 304L | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 8.0 g/cm3 | 40% | 1400 °C |
| SS 316 | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 8.0 g/cm3 | 35 % | 1454 °C |
| SS 316L | 485 Min | 170 Min. | 8.0 g/cm3 | 40 % | 1400 °C |
| Type | Peeled nd Ground | Cold Drawn and Polish | Peeled and Polished | Cold Drawn and Ground |
|---|---|---|---|---|
| Sizes (mm) | 20.00 – 50.00 | 3.00 to 75.00 | 40.00 – 150.00 | 10.00 to 75.00 |
| Sizes (inch) | 3/4 – 2.00 | 1/8 to3.00 | 1.50 – 6.00 | 5/6 to 2.50 |
| Tolerance | h9 to h11 | h8 to h11 | h11, h11-DIN 1013 | h8 to h11 |
| CD | CF | CG | BD | ST | P&T |
|---|---|---|---|---|---|
| Cold drawn | Cold finished | Centreless ground | Bright drawn | Smooth turned | Peeled and turned |
| P | HRAP | HF | SRE | PR | RT |
| Polished | Hot rolled annealed and pickled | Hot finished | Slit rolled edge | Peeled and reeled | Rough turned/peeled |
The typical lifespan of stainless steel forged bars varies based on usage, environment, and maintenance but generally lasts 20 to 50 years, with proper care, especially in corrosion-resistant conditions.
Yes, stainless steel forged bars and rods can be customized in size, including diameter, length, and shape, to meet specific requirements for various applications in industries like manufacturing and construction.
Stainless steel forged bars are considered environmentally friendly due to their recyclability, durability, and resistance to corrosion. They have a long lifespan, reducing the need for frequent replacements and minimizing waste.
Forged Stainless Steel Bars and Rods find application in stressful, corrosion-prone conditions like the aerospace, petrochemical, and naval industries. They are utilized in the production of shafts, valves, pump parts, fasteners, and turbine components. They find usage in the automobile industry for engine parts, suspension components, and structural components where high strength and durability are needed. Their high resistance to oxidation and corrosion render them suitable for chemical process equipment, heat exchangers, and offshore facilities. Stainless steel forged bars and rods are also commonly utilized in medical devices and food processing equipment because of their cleanliness and durability needs.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.