Kanish Metals, Dubai, UAE, is a known manufacturer and exporter of superior Aluminium 2014 Bars and Rods to industries requiring superior performance and strength. Aluminium 2014 is an alloy with high strength, which can be heat treated and finds extensive applications in the aerospace, defence, and heavy engineering fields because of its better mechanical properties and resistance. A popular choice for its superior machinability and stress-relieving properties, this alloy is particularly ideal for structural parts subject to heavy weight. Kanish Metals provides Aluminium 2014 bars and rods in a range of sizes and surface finishes, providing customized solutions to satisfy stringent industry needs with unmatched accuracy and quality.
Aluminium 2014 Bars and Rods mainly consist of aluminium mixed with 4.4% copper, as well as trace amounts of manganese, magnesium, and silicon. The alloy is exceptionally strong, with tensile strength measuring 470–570 MPa, yield strength of approximately 350 MPa, and a hardness value of up to 120 HB. It also responds favourably to heat treatment, which adds to its mechanical strength. Aluminium 2014 is stress corrosion cracking resistant and maintains strength even at high temperatures, albeit with lower corrosion resistance than more pure aluminium alloys. Surface treatments may be used to enhance its longevity in adverse environments.
| Aluminium Alloy | ASTM B211, B211, B565, B316 5082, AMS 4121 |
| Standard | ASTM, ASME, AMS, GB/T, JIS |
| Aluminium Round Bar Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium Bar Form | Aluminium Round, Hex, Flat, Half Round, Oval, Rectangular in Black & Bright Finish |
| Aluminium Round Bar Diameter | 0.1-600mm,etc |
| Aluminium Hexagonal Bar | 0.1-600mm,etc |
| Aluminium Angle Bar Size | 0.5mm*40mm*40mm-20mm*400mm*400mm |
| Aluminium Flat Bar Thickness | 0.1-600mm,etc |
| Aluminium Flat Bar Size | 1-2500mm, etc |
| Aluminium Round Bar Length | 1-12m, Random, Fix & Cut Length or as per clients’ requirement |
| Aluminium Bar | Bright, Polish & Black |
| Aluminium 2014 | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 0.7 | 0.50 – 1.20 | 0.2 – 0.8 | 0.4 – 1.2 | 3.9 – 5.0 | 0.25 | 0.15 | 93.5 |
| Material | Temper | Diameter (mm) | Tensile Strength min ((N/mm²) | Yield Strength (min) (N/mm²) | Elongation on 5.65 V (min) |
| 2014 Bar | T4 | <20 | 370 | 230 | 11 |
| 2014 Bar | T4 | 20-75 | 390 | 250 | 11 |
| 2014 Bar | T4 | 75-150 | 390 | 250 | 9 |
| 2014 Bar | T4 | 150-200 | 370 | 230 | 8 |
| 2014 Bar | T6510 | 20-75 | 480 | 435 | 7 |
| 2014 Bar | T6510 | 75-150 | 465 | 420 | 7 |
| 2014 Bar | T6510 | 150-200 | 435 | 390 | 7 |
| STANDARD | UNS | WERKSTOFF NR. |
| Aluminium 2014 | A92014 | 3.1255 |
| Size in mm | Average Weight | |
| KG/MTR | KG/FT | |
| 10 | 0.62 | 0.18 |
| 12 | 0.90 | 0.30 |
| 14 | 1.20 | 0.40 |
| 16 | 1.60 | 0.50 |
| 18 | 2.00 | 0.60 |
| 20 | 2.50 | 0.80 |
| 22 | 3.00 | 0.90 |
| 24 | 3.56 | 1.08 |
| 25 | 3.90 | 1.20 |
| 28 | 4.80 | 1.50 |
| 30 | 5.55 | 1.69 |
| 32 | 6.30 | 1.90 |
| 34 | 7.14 | 2.18 |
| 36 | 8.00 | 2.44 |
| 40 | 9.90 | 3.00 |
| 45 | 12.49 | 3.81 |
| 50 | 15.40 | 4.70 |
| 56 | 19.34 | 5.89 |
| 60 | 22.20 | 6.80 |
| 63 | 24.47 | 7.46 |
| 63.5 | 24.86 | 7.58 |
| 65 | 26.05 | 7.94 |
| 70 | 30.20 | 9.20 |
| 73 | 32.86 | 10.00 |
| 75 | 34.72 | 10.58 |
| 78 | 37.51 | 11.43 |
| 80 | 39.50 | 12.00 |
| 83 | 42.47 | 12.95 |
| 85 | 44.55 | 13.58 |
| 90 | 50.00 | 15.20 |
| 92 | 52.19 | 15.91 |
| 93 | 53.39 | 16.27 |
| 95 | 55.65 | 16.95 |
| 100 | 61.66 | 18.79 |
| 105 | 67.98 | 20.72 |
| 110 | 74.60 | 22.74 |
| 115 | 81.64 | 24.88 |
| 125 | 96.34 | 29.36 |
To maintain Aluminium 2014 bars, regularly clean them with mild soap and water to prevent corrosion. Avoid exposure to harsh chemicals and extreme temperatures, and inspect for signs of fatigue or wear.
Aluminium 2014 bars and rods are not ideal for high-temperature applications. While they offer high strength, their performance decreases at elevated temperatures, limiting their suitability for environments above 150°C (302°F).
Aluminium 2014 rods are sized by their diameter, typically ranging from small (e.g., 6 mm) to large (e.g., 100 mm), and are available in various standard or custom lengths.
Aluminium 2014 Bars and Rods find broad applications in the aerospace and defense industries in producing fuselage parts, wing spars, aircraft fittings, and fasteners due to their superior strength-to-weight ratio. They are also crucially involved in the development of rocket structures, missile parts, and military vehicles requiring high-performance materials. In the automotive sector, Aluminium 2014 finds application in engine components, transmission parts, and wheels. Due to its high tensile strength and durability, it is appropriate for machine components, tooling, and structural components in heavy industry. It is used where high stress resistance and precise engineering are needed and which performs steadily in the process.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.