Kanish Metals has built a solid reputation as a leading manufacturer and supplier of Stainless Steel 1.4122 Flat Bars in Dubai, UAE. Their products are known for top-notch quality, boasting impressive hardness, corrosion resistance, and durability. This particular stainless steel, also referred to as X39CrMo17-1 in EN standards, is a martensitic alloy enriched with chromium and molybdenum, which gives it exceptional resistance to wear, scaling, and moderately harsh environments. The flat bars made from this alloy are designed to offer high mechanical strength, precise dimensions, and long-lasting performance, making them perfect for demanding applications. Thanks to their state-of-the-art production facilities, rigorous quality checks, and prompt delivery, Kanish Metals has gained a reputation as a trustworthy supplier of Stainless Steel 1.4122 Flat Bars across various industries.
These flat bars consist of 15–17% chromium, 0.8–1.2% molybdenum, and 0.35–0.45% carbon, along with trace amounts of manganese and silicon. They provide a tensile strength ranging from 700 to 950 MPa and a yield strength of about 450 to 650 MPa, depending on the heat treatment process, along with excellent hardness and good wear resistance. This alloy ensures reliable stability and durability while maintaining oxidation resistance even at higher temperatures.
Standard : AISI, ASTM, BS, DIN, GB, JIS
Specification : ASTM A276 / ASME SA276
Diameter : 6mm-500mm
Width: 100-4200mm
Length : 1 to 6 meters & as per customer’s requirement.
Range : 3 MM TO 350 MM DIA
Dimensions: 5.5MM – 1100MM
Form : Round Bars, Square Bars
Materials Grades: Stainless Steel 1.4122
| Grade | C | Si | Mn | P | S | Cr | Mo | N | Others |
| SS 1.4122 | 0.33-0.45 | max 1.00 | max 1.5 | max 0.040 | max 0.015 | 15.5-17.5 | 0.80-1.30 | max 1.00 | – |
| Yield Rp0.2 (MPa) | Tensile Rm (MPa) | Impact KV/Ku (J) | Elongation A (%) | Reduction in cross section on fracture Z (%) | As-Heat-Treated Condition | Brinell hardness (HBW) |
| 869 (≥) | 926 (≥) | 41 | 44 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 |
| EN | DIN | AFNOR |
| 1.4122 | 1.4122 – X 39 Cr Mo 17 1 | Z 38 CD 16-01 |
Yes, Stainless Steel 1.4122 flat bars can be welded, though preheating and post-weld heat treatment may be necessary to reduce the risk of cracking and ensure optimal weld quality.
Yes, Stainless Steel 1.4122 flat bars can be heat treated. It is typically hardened by quenching and tempering, allowing control over hardness and strength for specific applications.
Stainless Steel 1.4122 flat bars resist corrosion due to their high chromium content, forming a passive oxide layer that protects the material from oxidation and corrosion in various environments.
Stainless Steel 1.4122 Flat Bars find their way into applications that require hardness, toughness, and wear resistance, along with moderate corrosion protection. You’ll often see them in pump shafts, turbine components, knives, surgical instruments, automotive parts, and precision tools. Their robust strength and durability make them ideal for use in power generation, petrochemical industries, and mechanical engineering. Additionally, they are utilized in marine hardware, food processing machinery, and structural components that operate under tough conditions. With an optimal blend of wear resistance, corrosion resistance, and mechanical strength, Stainless Steel 1.4122 Flat Bars are a dependable choice for a wide range of industrial and engineering applications.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.