Kanish Metals is a reliable maker and seller of 1141 cold drawn rods and bars in Dubai, UAE, delivering quality carbon steel products for uses that demand enhanced machinability and surface finish. With an emphasis on accuracy and consistency, Kanish Metals provides 1141 bars and rods in different sizes and lengths as per industry-specific requirements. The process of cold drawing increases dimensional tolerance, surface finish, and mechanical integrity, and these products are thereby fit for application in the automobile, machinery, and general engineering industries. Kanish Metals is recognized for its prompt delivery, technical know-how, and customer satisfaction commitment.
1141 cold drawn bars and rods are produced using a medium carbon manganese steel containing added sulfur for improved machinability. The standard chemical composition consists of around 0.48–0.53% carbon, 1.35–1.65% manganese, and 0.08–0.13% sulfur. Cold drawing clarifies grain structure, enhancing tensile strength and yield strength but with a good ductility. Mechanical properties are tensile strength of 655–860 MPa and yield strength of 415–620 MPa. The material is not generally employed for welding or shaping but shines in uses where machinability, straightness, and strength are significant demands.
Specification : IS 319 / IS 320
Grade : Grade 1 / 2 , HT 1 / 2
Range : 3mm to 152mm Dia
Length : 100 mm to 6000 mm
Form : Round, Square, Hex (A/F), Rectangle, Wire (Coil Form), Wire-mesh, Billet, Ingot, Forging Etc.
| Copper | 56.0 – 59.0% | ||
| Lead | 2.0 to 3.50% | ||
| Iron | 0.35% max. | ||
| Total Imp. Excl. Iron | 0.70% max. | ||
| Zinc | Remainder | ||
| Element | Value |
| Yield Stress | 150 MPa Min. |
| Tensile Strength | 380 MPa Min. |
| Hardness Brinell | 90 to 160 HB |
| Elongation | 18 Min. |
| Condition | Size | T.S. MPA | EL% Min |
| Annealed (O) | 6-25 25-50 50 above | 345 315 285 | 12 17 22 |
| Half-Hard (HB) | 6-12 12-25 25-50 50 above | 405 395 355 325 | 4 6 12 17 |
| Hard (HD) | 6-12 12-25 | 550 490 | – 4 |
Yes, brass rods are highly suitable for machining due to their excellent machinability. They offer smooth cutting, good strength, and corrosion resistance, making them ideal for various mechanical applications.
Yes, brass rods can be welded, but it requires proper technique and equipment. Due to their high copper content, brass can be prone to oxidation and cracking during welding.
The hardness of brass rods typically ranges between 60-100 HRB (Rockwell B scale), depending on the specific alloy and temper, with harder grades reaching up to 150 HB (Brinell hardness).
1141 cold drawn rod and bar are extensively utilized in components demanding high strength, good machinability, and reliable dimensional tolerances. They are particularly well suited for making components like pins, shafts, studs, fasteners, bushings, and machine parts. For the automotive and industrial machinery industries, 1141 is appreciated for its precision-machining ability into close tolerances. Cold drawing achieves a smooth surface finish, so it is acceptable for components that have minimal post-processing. Still, it should be avoided in applications where welding or heavy forming is involved as it contains sulfur.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.